Flame retardants and compositions containing them

ABSTRACT

Flame retardants having good stability at the processing temperatures of high melting polymers are described. The flame retardants are halogen-containing bis-imides, for example, those of the formula ##STR1## R and X being defined in the specification.

BACKGROUND OF THE INVENTION

This invention relates to compositions comprising a flammable material and a flame retardant. More especially, it relates to compositions comprising macromolecular flammable materials, for example, polymers. The invention also relates to flame retardants and a process for their manufacture.

The problem of the flammability of certain materials has received considerable attention. One method by which the flammability of certain materials, especially macromolecular materials, has been reduced is by the incorporation therein of halogen-containing compounds, both inorganic and organic. Inorganic halogen-containing compounds often have deleterious effects on the properties of the materials, or damage the equipment in which the materials are processed, because of their corrosive nature, and therefore organic halogen-containing compounds, often in combination with inorganic oxides or non-halogenated salts, have been used most extensively.

While the previously proposed organic halogen-containing compounds have been accepted, many disadvantages are still associated with their use. Many previously proposed flame retardants have been more or less volatile, leading to loss in flame retardance during use of articles containing them, as well as in processing. As macromolecular materials having higher use temperatures (and, accordingly, higher processing temperatures) have been developed, the disadvantages of volatile additives become more marked. In addition, such higher use and processing temperatures have shown up deficiencies in the thermal stability of many of these previously proposed organic halogen-containing flame retardants. Thus, many compounds which have been readily incorporated in materials processed at 150° C. have failed due to volatilization, sublimation or decomposition when incorporated into a material which is processed at temperatures in the region of 250° C. to 350° C. Further, some of the commercial materials are adversely affected by the radiation making them unsuitable for incorporation into compositions which are to be irradiation crosslinked.

Some additives may, for example, be sensitive to water even when incorporated into the material, and when additive-containing compositions are tested with boiling water, the organic compound is dissolved out or hydrolyzed, resulting at best in impaired flame retardance, and often also in corrosion by the hydrolysis products, for example, the halogen acids, resulting from contact with water. Such water sensitivity also shows when the composition is in prolonged contact with a humid atmosphere.

SUMMARY OF THE INVENTION

It is an object of this invention to provide flame retarded compositions which can be processed at elevated temperatures.

It is a further object of the invention to provide a flame retardant having low volatility, good thermal stability and low sensitivity to water.

Other objects of the invention will be apparent from the following description of the invention.

Briefly, the present invention provides a composition comprising a flammable material and a halogen-containing bis-imide. The bis-imides suitable for use in this invention advantageously contain bromine, chlorine, or both of these halogens; bromine-containing compounds are preferred. Advantageously, the halogen atoms are bonded to carbon atoms, the carbon atoms preferably being aromatic carbon atoms, for example, members of a benzene ring.

Advantageously, the bis-imide contains at least 4, preferably at least 8, halogen atoms, preferably at least 4 bromine atoms, which are, as stated above, advantageously bonded to carbon atoms in an aromatic ring. Advantageously, the halogen atoms represent at least about 25% by weight of the molecule.

It will be apparent to those skilled in the art that no precise values for the proportion of the bis-imides in the composition can be given, since this proportion will vary with the particular flammable material, the presence of other additives, the particular bis-imide, and the degree of flame retardance sought in any given application. Further, the proportion necessary to achieve a given extent of flame retardance in a particular composition will depend on the shape of article into which the composition is to be made, for example, electrical insulation, tubing and film will each behave differently. In general, however, the composition may contain from about 5% to about 40%, preferably 20% to 30%, of a bis-imide of the present invention, when the bis-imide is the only flame retardant compound in the composition.

It will be appreciated that one or more bis-imides may be incorporated in the same composition and that other flame retardant materials may be used in conjunction with the bis-imides. It is especially advantageous to use the bis-imide and a compound, especially the oxide, of a Group V element, for example, bismuth, arsenic, phosphorus and especially antimony, in a composition. Of these compounds, antimony oxide is especially preferred. If such a compound is present in a composition, the quantity of bis-imide needed to achieve a given flame-retardance is accordingly reduced.

Accordingly, the present invention also provides a flame retardant system comprising a bis-imide in admixture with a compound of a Group V element, and compositions comprising a flammable material and such a flame-retardant system. The proportions of the bis-imide and the compound are not critical, but in general the bis-imide and the compound are conveniently in a ratio of from about 1:5 to about 15:1, preferably 1:1 to 9:1.

The compositions may contain up to about 40% by weight of the system, preferably between 20% and 30% by weight. It is believed that the inorganic compound and the halogen-containing bis-imide will react under the conditions of combustion of a flammable material to form inorganic halogen compounds, e.g., halides and oxyhalides, which assist in retarding combustion. To the extent that the two components of the system interact, they should be present in approximately equivalent proportions. The halogen-bearing component also acts as a flame retardant independently and the proportions in a flame retardant system are a matter of choice, depending, inter alia, on the material in which the system is to be incorporated, and commercial considerations. Thus, a mixture in which one component predominates may be regarded as a mixture of equivalent quantities of the two components blended with the one in excess.

The flame retardant bis-imides and systems containing bis-imides may be used in combination with virtually any flammable material. The material may be macromolecular, for example, a cellulosic material or a polymer. Among polymers with which the bis-imide may be combined there may be mentioned, by way of illustrative examples, olefin polymers, for example, homopolymers of ethylene, propylene, butene, copolymers of two or more such monomers and copolymers of one or more such monomers with other copolymerizable monomers, for example, ethylene/propylene copolymers, ethylene/ethyl acrylate copolymers and ethylene/vinyl acetate copolymers; polymers of olefinically unsaturated monomers, for example, polystyrene and styrene copolymers; polyurethanes; polyamides, polyimides; acrylic resins, polyesters, epoxy resins; alkyds; phenolics; elastomers, for example, butadiene/styrene copolymers, butadiene/acrylonitrile copolymers and terpolymers of acrylonitrile, butadiene and styrene; natural rubber; butyl rubber; and polysiloxanes. The compositions may contain any of the additives usually present and where appropriate to the particular polymers, may be crosslinked by chemical means or by irradiation.

The bis-imides of the present invention advantageously have one of the following general formulae ##STR2## wherein R₁, R₂ and R₃, which may be the same or different, each represent a divalent organic radical, R₄ and R₆, which may be the same or different, each represent a monovalent organic radical, R₅ represents a tetravalent organic radical and R₇ represents a trivalent organic radical, and wherein R₁, R₂ and R₃ in Formula I, R₄, R₅ and R₆ in Formula II, and R₁, R₇ and R₄ in Formula III taken together contain at least one halogen atom, preferably at least 4 halogen atoms, advantageously chlorine or bromine atoms, preferably bromine. Advantageously, the halogen atoms represent at least 25% by weight of the molecule and preferably, the halogen atoms are bound to aromatic carbon atoms.

For synthetic reasons, bis-imides of Formulae I and II are preferred, especially Formula I, as are bisimides in which (in Formula I) R₁ and R₃ are identical, and (in Formula II) R₄ and R₆ are identical; it is to be understood, however, that the flame retardant effect of the bis-imides is in no way dependent on their being identical. Furthermore, mixtures of one or more compounds of one or more of each of the above formulae may be employed.

Subject to the requirement that the bis-imides be halogen-containing, radicals R₁ to R₇ preferably represent radicals such that R₁ (COOH)₂ and R₃ (COOH)₂ are each one of the following:

tetrabromophthalic acid

tetrachlorophthalic acid

1,4,5,6,7,7-hexachlorobicyclo-(2.2.1)-5-heptene-2,3-dicarboxylic acid (chlorendic acid)

5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano naphthalene-2,3-dicarboxylic acid

5,6,7,8,9,9-hexabromo-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano naphthalene-2,3-dicarboxylic acid

phthalic acid

succinic acid

dichloromaleic acid

R₂ (NH₂)₂ is one of the following:

ethylenediamine

1,6-hexamethylenediamine

4,4'-methylenedianiline

4,4'-oxydianiline

phenylenediamines

xylylenediamines

tetrachloroxylylenediamines

tetrabromoxylylenediamines

R₄ NH₂ and R₆ NH₂ are one of the following:

2,4,6-trichloroaniline

2,4,6-tribromoaniline

2,3,4,5,6-pentabromobenzylamine

2,3,4,5,6-pentachlorobenzylamine

R₅ (COOH)₄ is one of the following:

pyromellitic acid

naphthalene-1,4,5,8-tetracarboxylic acid

R₇ (NH₂)(COOH)₂ is one of the following:

3- or 4-aminophthalic acid

or imide-forming isomers or substitution products of any of the above amides or acids. Further diamines and the dianhydrides of further tetracarboxylic acids are those listed in U.S. Pat. No. 3,179,632, the disclosure of which is incorporated herein by reference.

Thus, the compounds mentioned above may be substituted, or further substituted, by halogen atoms, especially by chlorine or bromine atoms, provided that imides may still be formed therefrom. The compounds may also be substituted by other groups, for example, alkyl, aryl, alkaryl or aralkyl radicals, functional groups and hetero atoms provided that the flame retardant properties of the resulting bisimides are not adversely affected thereby. It will be appreciated that where water sensitivity is undesirable the bis-imide will not contain groups which would tend to make the bis-imide more water-soluble. It will also be appreciated that the presence of a substituent group on the radical will not in general affect the flame retardant properties except to the extent that the molecular weight is increased. Such an increase in molecular weight would in general mean that a greater weight of bis-imide is necessary to achieve a given degree of flame retardance in a composition; on the other hand, the change in melting point and volatility resulting from the presence of, for example, an additional methyl or ethyl group in the molecule may well be desirable and offset the increase in molecular weight and decrease in proportion of halogen in the molecule.

As illustrative examples of suitable bis-imides, there may be mentioned

N,N'-(p and m-phenylene)-bis[3,4,5,6-tetrachlorophthalimide]

N,N'-(p and m-phenylene)-bis[3,4,5,6-tetrabromophthalimide]

N,N'-(methylene-di-p-phenylene)-bis[3,4,5,6-tetrachlorophthalimide]

N,N'-(methylene-di-p-phenylene)-bis[3,4,5,6-tetrabromophthalimide]

N,N'-(oxy-di-p-phenylene)-bis[3,4,5,6-tetrachlorophthalimide]

N,N'-(oxy-di-p-phenylene)-bis[3,4,5,6-tetrabromophthalimide]

N,N'-(p and m-phenylene)-bischlorendimide

*N,N'-(p and m-tetrachloroxylylene)-bis[3,4,5,6-tetrachlorophthalimide]

*N,N'-(p and m-tetrachloroxylylene)-bis[3,4,5,6-tetrabromophthalimide]

*N,N'-(p and m-tetrachloroxylylene)-bischlorendimide

N,N'-(1,2-ethylene)-bischlorendimide

N,N'-(1,2-ethylene)-bis[3,4,5,6-tetrabromophthalimide]

N,N'-bis(1,2,3,4,5-pentabromobenzyl)-pyromellitimide

N,N'-bis(2,4,6-tribromophenyl)-pyromellitimide

Certain of these compounds are novel and the present invention accordingly also provides halogen-containing bisimides (other than those formed from tetrachlorophthalic anhydride and p,p'-diaminodiphenylmethane and 2,4-diaminotoluene), especially compounds of the formula ##STR3## in which R represents a divalent aliphatic, aromatic or araliphatic radical which may be substituted by one or more halogen atoms or interrupted by hetero atoms. Preferably R, when it is an aliphatic radical, is an alkylene radical and preferably it contains from 1 to 18 carbon atoms, especially from 2 to 10 carbon atoms. When R is an aromatic radical, it may contain 1, 2 or more ring systems which may be joined, when there are two or more, by aliphatic radicals, by hetero atoms, especially oxygen, or directly; the imide nitrogen atoms may be bonded directly to the aromatic system or by an alkylene chain. The aromatic rings may advantageously be substituted by one or more halogen atoms, preferably by bromine and especially by chlorine atoms.

More especially, the present invention provides compounds of the Formula IV in which R represents a radical of the formula ##STR4## in which each R₈, which may be the same or different, represents hydrogen, an alkyl radical containing from 1 to 4 carbon atoms, or a halogen atom, R₉ represents an alkylene radical, preferably containing 1 carbon atom, or hetero atom or group, preferably oxygen, or is absent, R₁₀ represents an alkylene radical having from 1 to 4 carbon atoms or is absent, and R₁₁ represents an alkylene radical having from 1 to 18, preferably 2 to 10, carbon atoms.

The bis-imides may be made by any of the methods in general use or described in the literature for the manufacture of imides. In general, the imide results from heating together the corresponding anhydride and amine with elimination of water, the reactants being dissolved in a common solvent. Suitable solvents include, for example, N-methyl-2-pyrrolidone, dimethylacetamide, xylene and cresol.

Generally, the imide will be precipitated from the solution either during the reaction or on cooling after reaction. If the imide is required pure, the precipitate may be filtered, washed, and recrystallized from a suitable solvent.

The bis-imides may be incorporated with the flammable material by any of the methods normally employed for the admixture of additives to the material. For example, when the flammable material is a polymer, the bis-imides, which are solid at room temperature and may generally be obtained in the form of powders, may be blended with granules, pellets, chips or a powder of the polymer in a tumbler or milled into a composition of the polymer and additives.

The invention will now be illustrated in the following examples, in which all parts are by weight unless otherwise indicated.

EXAMPLE 1 Preparation of N,N'-(2,4,5,6-tetrachloro-m-xylylene)-bis-chlorendimide

A 1 liter flask was equipped with a nitrogen purge, a heating mantle, a mechanical stirrer, a reflux condenser and a Dean-Stark apparatus (a graduated vessel which allows the volume of water in the condensate to be measured). To 81.6 gms (0.22 mole) of 1,4,5,6,7,7-hexachlorobicyclo-(2.2.1)-5-heptene-2,3-dicarboxylic anhydride (chlorendic annydride) was added 27.4 gms (0.1 mole) of 2,4,5,6-tetrachloro-m-xylylenediamine in 500 ml. xylene. The mixture was refluxed (at about 140° C.) for 2 hours, after which the reaction mixture was a clear solution, 3.2 ml. of water having been collected in the Dean-Stark apparatus. The solvent was then boiled off, precipitation occurring when about 450 ml. of xylene had been removed. The remaining slurry was cooled and filtered to yield fine white crystals which were washed with methanol. Addition of methanol to the filtrate yielded a second crystalline precipitate; the infrared (IR) spectra of the two compounds were identical. The first compound (62.1 gms) had a melting point of 293°-296° C., the second compound (6.9 gms) melted at 285°-290° C., indicating a lower purity. The IR spectrum was indicative of an imide and showed no amide absorption. The total yield was 68%.

    ______________________________________                                         Analysis: C.sub.26 H.sub.8 Cl.sub.16 N.sub.2 O.sub.4                                         Calc. %                                                                               Found %                                                   ______________________________________                                         Carbon          31.9     31.8                                                  Hydrogen        0.8      1.3                                                   Nitrogen        2.9      3.0                                                   Chlorine        57.9     58.3                                                  ______________________________________                                    

EXAMPLE 2 Preparation of N,N'-(p-phenylene)-bis[3,4,5,6-tetrachlorophthalimide]

In a 5 liter round-bottom flask equipped with a heating mantle, a stirrer, a thermometer, a condenser and a nitrogen purge, there were reacted 457.5 grams (1.6 mole) of tetrachlorophthalic anhydride and 86.5 gms (0.8 mole) of p-phenylenediamine in 2000 ml. of N-methyl-2-pyrrolidone (NMP), the reactants going into solution as the mixture was heated with stirring. At 170° C., precipitation began and continued as the temperature was raised to 200° C. where it was maintained for 90 minutes. The reaction mixture was then allowed to cool overnight. The cooled mixture was filtered and the yellow precipitate was recovered. The precipitate was washed with NMP, thoroughly stirred in acetone, filtered and washed with more acetone. The product was dried under vacuum at 150° C. for 16 hours. 272.7 gms (yield=53%) of an ivory-yellow material was obtained, having a melting point in excess of 500° C., with some sublimation at about 425° C. The IR spectrum had the characteristics of an imide with the absorption bands at 1710s and 1770w cm⁻¹. The product was insoluble in water.

    ______________________________________                                         Analysis: C.sub.22 H.sub.4 Cl.sub.8 N.sub.2 O.sub.4                                          Calc. %                                                                               Found %                                                   ______________________________________                                         Carbon          41.0     41.5                                                  Hydrogen        0.6      0.7                                                   Nitrogen        4.4      4.5                                                   Chlorine        44.0     44.7                                                  ______________________________________                                    

EXAMPLE 3 Preparation of N,N'-(p-phenylene)-bis[3,4,5,6-tetrabromophthalimide]

108 gms (1.0 mole) of p-phenylenediamine was dissolved in 1 liter of warm NMP under a nitrogen atmosphere and the solution filtered to remove suspended particles. This filtered solution was then added to a similarly prepared filtered solution of 928 gms (2.0 moles) of tetrabromophthalic anhydride in 2 liters of warm NMP in the apparatus described in Example 2. A mildly exothermic reaction took place and the mixture was further heated while stirring. At about 145° C., precipitation began. The quantity of brown precipitate increased with continued heating and a further 2 liters of NMP was added to facilitate stirring, the temperature being raised to 200° C. and maintained for 2 hours, before the mixture was allowed to cool. The precipitate was collected, washed with NMP, roughly dried and washed with acetone. The material was then stirred well with acetone, filtered and again washed before being dried overnight at 150° C. under vacuum. The product was a fine, rusty-gold precipitate with a melting point above 500° C. The yield was 486 gms (49%), the infrared spectrum having the characteristic imide structure, absorption bands at 1712s and 1765w cm⁻¹. The compound was insoluble in water, methanol, ether, xylene, dimethyl sulphoxide and dimethyl acetamide.

    ______________________________________                                         Analysis: C.sub.22 H.sub.4 Br.sub.8 N.sub.2 O.sub.4                                          Calc. %                                                                               Found %                                                   ______________________________________                                         Carbon          26.4     26.7                                                  Hydrogen        0.4      0.5                                                   Nitrogen        2.8      2.9                                                   Bromine         64.0     63.2                                                  ______________________________________                                    

The nonvolatility of the product was demonstrated by subjecting the product to a vacuum (1×10⁻⁶ torr.) at a temperature of 300° C. and analyzing the gas in contact with the product by mass spectography. No trace of the product in the gas was found.

EXAMPLES 4 TO 22

The following compounds were prepared under conditions generally similar to those of Example 1, 2 or 3.

                                      TABLE I                                      __________________________________________________________________________     Ex.           Time                                                                              Temp.    Product Yield                                                                              MP                                       No.                                                                               Bis-Imide From:                                                                           Hrs.                                                                              °C.                                                                         Solvent                                                                             Character                                                                              %   °C.                               __________________________________________________________________________      4 Chlorendic anhydride                                                                      1  120 Xylene                                                                              Fine white                                                                             85  342-45                                      and MPD                crystals                                              5 Chlorendic anhydride                                                                      1.5                                                                               140 Xylene                                                                              Lavender                                                                               71  >475                                        and PPD                precipitate                                           6 Chlorendic anhydride                                                                      0.5                                                                               140 Xylene                                                                              White   88  328-30                                      and PXD                precipitate                                           7 Chlorendic anhydride                                                                      0.5                                                                               125 Xylene                                                                              White   68  354-56                                      and ED                 crystals                                              8 Tetrachlorophthalic                                                                       0.5                                                                               140 Xylene                                                                              Yellow  95   405                                        anhydride and MPD      precipitate                                           9 Tetrachlorophthalic                                                                       1.0                                                                               195 NMP  Yellow  33  400-10                                      anhydride and MXD      precipitate                                          10 Tetrachlorophthalic                                                                       2.5                                                                               200 NMP  Yellow  19  465 dec                                     anhydride and PXD      precipitate                                          11 Tetrabromophthalic                                                                        2.5                                                                               200 NMP  Fluffy yellow                                                                          44  454-58                                      anhydride and MPD      precipitate                                          12 Tetrabromophthalic                                                                        0.5                                                                               175 NMP  Ivory   57   445                                        anhydride and MXD      precipitate                                          13 Tetrabromophthalic                                                                        2.5                                                                               200 NMP  Yellow ivory                                                                           18  436-40                                      anhydride and PXD      precipitate                                          14 Tetrabromophthalic                                                                        2.5                                                                               200 NMP  Yellow  57  390-95                                      anhydride and MD       precipitate                                          15 Tetrabromophthalic                                                                        2.5                                                                               200 NMP  Yellow  29  410-15                                      anhydride and OD       precipitate                                          16 Tetrabromophthalic                                                                        0.5                                                                               200 NMP  Yellow  26  465 dec                                     anhydride and ED       precipitate                                          17 Tetrachlorophthalic                                                                       0.5                                                                               175 NMP  Light yellow                                                                           58  367-70                                      anhydride and MD       precipitate                                          18 Tetrachlorophthalic                                                                       0.5                                                                               160 DMA  Yellowish                                                                              44  380-83                                      anhydride and OD       precipitate                                          19 Phthalic anhydride                                                                        1.0                                                                               180 NMP  Fine white                                                                             86  285-87                                      and MXD                crystals                                             20 Chloran and PPD                                                                           0.5                                                                               135 Xylene                                                                              Lavender                                                                               45  400 dec                                                            precipitate                                          21 Chloran and PXD                                                                           1.0                                                                               180 NMP  Off-white                                                                              83  410 dec                                                            powder                                               22 Pyromellitic                                                                              17.0                                                                              200 NMP  White powder                                                                           91  >500                                        dianhydride and                                                                pentabromobenzyl-                                                              amine                                                                       __________________________________________________________________________      Where                                                                          ED represents ethylenediamine                                                  MD represents 4,4methylenedianiline-                                           OD represents 4,4oxydianiline-                                                 MPD represents                                                                 PPD represents -pphenylenediamine-                                              MXD represents                                                                PXD represents                                                                 NMP represents N--methyl2-pyrrolidone                                          DMA represents N,N'--dimethylacetamide                                         Chloran represents                                                             2,3dicarboxy-5,8-endomethylene-5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-o     tahydronaphthalene anhydride                                              

EXAMPLE 23 Preparation of p-(3,4,5,6-tetrabromophthalimide)-p'-(3,4,5,6-tetrachlorophthalimide)-diphenylmethane:

A heated solution of 13.24 gms (0.046 mole) of 3,4,5,6-tetrachlorophthalic anhydride in 25 ml. xylene was added to a heated solution of (26 gms, 0.041 mole) p-amino-p'-(3,4,5,6-tetrabromophthalimide)-diphenylmethane in 425 ml. xylene and the mixture refluxed for 4.5 hours. A yellow precipitate was filtered from the hot reaction mixture, washed in turn with hot xylene and methanol and dried under vacuum at 100° C. The yield was 7.7 gms (21%). After two recrystallizations from dimethylacetamide and methanol, the melting point was 383° C., with decomposition.

The p-amino-p'-(3,4,5,6-tetrabromophthalimide)-diphenylmethane was prepared as follows: 148.5 gms (0.25 mole) of 4,4'-methylenedianiline was dissolved in 400 ml. of hot xylene, 115.7 gms (0.25 mole) of 3,4,5,6-tetrabromophthalic anhydride was dissolved in a second sample of hot xylene and the two solutions mixed, stirred under reflux for 2 hours, and allowed to stand overnight. The mixture was then reheated to boiling, the remaining solid filtered, washed with xylene and methanol, and dried at 100° C. under vacuum. Recrystallization from xylene gave dark orange crystals. On heating the solid, it darkens at 240° C., decomposition appearing complete at 340° C. Infrared analysis shows bands corresponding to NH₂ (3450 and 1628 cm⁻¹) and imide (1720 and 1765 cm⁻¹) groups.

EXAMPLE 24 Preparation of N,N'-(2,3,5,6-tetrachloro-p-xylylene)-bis-phthalimide

In a 3 liter, round-bottom flask equipped with a heating mantle, mechanical stirrer, thermometer, nitrogen inlet and condenser, 137 gms (0.5 mole) of 2,3,5,6-tetrachloro-p-xylylenediamine was dissolved at room temperature in 1 liter N-methyl-2-pyrrolidone (NMP). While stirring, 150 gms (1.0 mole) solid phthalic anhydride was added, the temperature rising to 47° C. The resulting greenish solution was heated to 180°-185° C. for 30 minutes, after which period crystallization took place. The hot mixture was poured into a 2 liter beaker when mass crystallization occurred.

After cooling to room temperature, the tan crystalline mass was filtered, washed with NMP, slurried with acetone and refiltered. After partial air drying, the crystals were dried in a vacuum over for 2.5 hours at 110° C. Yield was 227.9 gms (85%), melting point, 328°-330° C.

    ______________________________________                                         Analysis: C.sub.24 H.sub.12 Cl.sub.4 N.sub.2 O.sub.4                                         Calc. %                                                                               Found %                                                   ______________________________________                                         Carbon          53.88    54.64                                                 Hydrogen        2.41     2.30                                                  Nitrogen        5.24     5.41                                                  Chlorine        26.51    26.51                                                 ______________________________________                                    

In the following examples, the symbols have the following meanings:

    ______________________________________                                         A         =     perchloropentacyclo[5.2.1.0.sup.2,6 -                                          .0.sup.3,9.0.sup.5,8 ]decane                                   B         =     1,4,7,10-dimethanocycloocta-1,2,                                               3,4,7,8,9,10,13,13,14,14-dodeca-                                               chloro-1,4,4a,5,6,6a,7,10,10a,                                                 11,12,12a-dodecahydro[1,2,5,6]                                                 dibenzene                                                      ______________________________________                                    

Example 1, etc.=product of Example No. 1, etc.

EXAMPLE 25

Compounds of the invention were blended with poly(1,12-dodecamethylene pyromellitimide) and produced as described in a copending application filed on even date with this application by Edward C. Stivers entitled "Polymers, Process and Articles", the disclosure of which is incorporated herein by reference. This is a high-melting polymer which is processed at temperatures in excess of 300° C., a temperature at which many flame retardants decompose. Compositions containing the polymer, 2% Irganox 1010 (an antioxidant-pentaerythritol tetra-3,5-ditert.butyl-4-hydroxydihydrocinnamate) and a compound of the invention were pressed into slabs of dimensions 4.0"×0.25"×0.05" at 330° C. and tested according to ASTM D635-63, but modified to test 4 strips of each composition having the given dimensions. This test, in which a Bunsen flame is contacted with one end of the strip, is used to compare the flammability of different materials. A short time to self-extinction, or a small extent or rate of burning, indicates good flame retardant properties.

                  TABLE II                                                         ______________________________________                                                  Additive Sb.sub.2 O.sub.3                                                                        Aver. Sec. to                                       Additive PHR      PHR      Self-Extinction                                                                          Dripping                                  ______________________________________                                           0       0        0       Burnt     Yes                                       Example 2                                                                               20       10       5         No                                        Example 2                                                                               30       15       0         No                                        Example 3                                                                               25        0       1         No                                        Example 22                                                                              25        0       2         No                                        Example 24                                                                              30       16       2         No                                        ______________________________________                                    

A similar slab containing 20 PHR of compound B was also prepared. This slab was black, indicating considerable decomposition of the commercial flame retardant.

EXAMPLE 26

Various compositions of low density polyethylene containing no flame retardant, commercially available flame retardants and the flame retardants of the present invention were prepared. The flammability of slabs 0.060" thick prepared from the compositions was measured according to ASTM D635-63, but modified to test 4 samples of each composition.

                  TABLE III                                                        ______________________________________                                                             Average Burning                                            Run            Additive Sb.sub.2 O.sub.3                                                                       Extent                                                                               Rate                                     No.  Additive  PHR      PHR     (in.) (in./min.)                               ______________________________________                                         1    O          0        0      3.00  1.24                                     2    A         10       20      2.65  1.06                                     3    A         20       10      3.00  0.84                                     4    B         10       20      2.45  0.93                                     5    B         15       15      1.32  0.75                                     6    B         20       10      0.25  0.55                                     7    B         30        0      3.00  0.89                                     8    Ex. 1     10       20      2.00  0.72                                     9    Ex. 1     20       10      0.45  0.53                                     10   Ex. 3     15       15      0.90  0.84                                     11   Ex. 3     20       10      0.25  0.36                                     12   Ex. 3     25        5      0.05  0.27                                     13   Ex. 3     27        3      0.40  0.32                                     14   Ex. 3     28        2      0.50  0.49                                     15   Ex. 3     30        0      0.98  0.47                                     16   Ex. 16    20       10      0.10   0.55*                                   17   Ex. 3     20       10      0.30   0.47*                                   ______________________________________                                          *These samples contained 0.3 parts per hundred resin of Santonox R             [4,4thiobis(6-tert-butyl-.sub.--mcresol)].                               

The reduction in both the rate and extent of burning compared with compositions containing no flame retardant and commercially available flame retardants can be seen. There was no dripping from any sample containing a flame retardant.

EXAMPLE 27

The following compositions were prepared and formed into slabs 0.060" thick.

    ______________________________________                                                            Parts by Weight                                             ______________________________________                                         Polyethylene (low density DFD                                                                       100                                                       6040)                                                                          2-hydroxy 4- -n-octoxybenzophenone                                                                  0.1                                                       (Cyosorb UV 531 light asborber)                                                4,4'-thiobis(6-tert-butyl- .sub.--m-cresol)                                                         0.1                                                       (Santonox R)                                                                   Flame retardant      See Table IV                                              ______________________________________                                    

50% of the slabs were irradiated to a dose of 15 Mrad from each side. All slabs were tested as in Example 26.

                  TABLE IV                                                         ______________________________________                                                              Average Burning                                           Run              Additive Sb.sub.2 O.sub.3                                                                      Extent                                                                               Rate                                    No.  Additive    PHR      PHR    (in.) (in./min.)                              ______________________________________                                              Unirradiated                                                              1    O            0       0      3.00   1.54**                                 2    B           20       10     0.75  0.43                                    3    B           30       0      3.00  1.02                                    4    Ex. 3       20       10     0.38  0.66                                    5    Ex. 3       30       0      0.32  0.62                                         Irradiated                                                                6    O            0       0      3.00   1.89**                                 7    B           20       10     2.40  0.63                                    8    B           30       0      3.00   1.14*                                  9    Ex. 3       20       10     0.82  0.41                                    10   Ex. 3       30       0      0.38   0.76*                                  ______________________________________                                          **In these tests, dripping of melted material took place.                      *In these tests, there was slight dripping of melted material.           

Table IV shows the superiority of the flame retardant of the present invention, especially in the irradiated polyethylene. It will be noted also that the flame retardant of the present invention is effective in reducing the rate and extent of burning in the absence of any antimony oxide or similar additive.

EXAMPLE 28

The product of Example 14 was incorporated into an acrylonitrile-butadiene-styrene polymer (CYCLOLAC X-27, made by Marbon Chemical, Division of Borg-Warner Corporation), and slabs of dimensions 5.0"×0.5"×0.06" were tested according to ASTM D635-63, modified to test four samples.

                  TABLE V                                                          ______________________________________                                                    Additive Sb.sub.2 O.sub.3                                           Additive   PHR      PHR        Results                                         ______________________________________                                         0           0       0          Burnt at 2.3"/min.                              Ex. 14     25       12.5       Non-burning;                                                                   3-5 sec. afterglow                              ______________________________________                                    

EXAMPLE 29

Two compounds of the invention were incorporated into polypropylene (Shell W550, a polymer stated to be especially suitable for articles which will be exposed to elevated temperatures), the composition was pressed into slabs 5.0"×0.5"×0.06", and tested according to ASTM D635-63.

                  TABLE VI                                                         ______________________________________                                                        Average Burning                                                        Additive  Sb.sub.2 O.sub.3                                                                       Extent Rate                                           Additive                                                                              PHR       PHR     (in.)  (in./min.)                                                                            Dripping                                ______________________________________                                         0      0         0              1.2    Yes                                     Ex. 14 26.7      13.3    0.3           No                                      Ex. 1  20        10      0.8           Slight                                  ______________________________________                                    

In general, those compounds of the present invention containing bromine atoms bound to aromatic carbon atoms have higher flame retardance and lower thermal stability than a corresponding compound containing chlorine atoms. It is also believed that in general the thermal stability of a compound containing a halogen atom bound to an aliphatic carbon atom is lower than that of a similar compound containing the same halogen atom bound to an aromatic carbon atom. These differences enable the user to choose a compound of the invention suitable for a particular purpose. The compounds of this invention can be processed at temperatures which will cause the decomposition of many commercially available materials.

It is believed that the stability of the compounds of this invention at processing temperatures of polymer materials is in part due to their being solid at these temperatures, and accordingly those compounds having melting points in excess of about 275° C. are preferred.

It is to be understood that all halogen-containing bis-imides are the subject of this invention, and that the foregoing examples are intended to be by way of illustration only and that the compounds of the invention can be used to flame retard a variety of materials other than the polymers hereinbefore described, these compositions indicating only some exemplary compositions in which the bis-imides have been found especially effective. It is also clearly to be understood that mixtures of two or more bis-imides may be employed when practicing this invention. The bis-imides can be combined with the materials commonly used or proposed for use as flame retardant synergists without departing from the ambit of the invention. Thus, the invention is to be regarded as limited only by the lawful scope of the appended claims. 

I claim:
 1. A composition comprising a flammable material and a chlorine-containing bisimide of the formula: ##STR5## wherein R is ##STR6## wherein each X is independently, hydrogen or chlorine with at least four X's being chlorine, n is 0-2, p is 0-1; and R' is ##STR7## where n=2-18 with the proviso that when p is O, R' is ##STR8##
 2. A composition comprising a flammable material and a compound of the formula ##STR9## in which R is selected from the group consisting of C₂ -C₄ alkylene, phenylene and ##STR10## where Z is oxygen.
 3. A composition comprising a flammable material and a compound of the formula ##STR11## in which R is selected from the group consisting of C₂ -C₄ alkylene, phenylene and ##STR12## wherein Z is oxygen and X is hydrogen or chlorine, at least 4 X's being chlorine.
 4. A composition of matter comprising a polymer and a chloroaryl imide of a polychloro-substituted polyhydropolycyclicdicarboxylic acid having the formula: ##STR13## in which A, X, and Y are independently selected from the group consisting of hydrogen or chlorine, at least one A and two X's being chlorine; Z is selected from the group consisting of oxygen, sulfur, amino and lower alkyl radicals; m is an integer of from 1 to 2; n ranges from 0 to 2; and p ranges from 0 to
 1. 5. The composition of matter as set forth in claim 4 in which said chloroaryl imide of a polychloro-substituted polyhydropolycyclicdicarboxylic acid is present in said composition of matter in a range of from about 5% to about 50% by weight of the composition of matter.
 6. The composition of matter as set forth in claim 4 in which said polymer compound is polypropylene and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is α,α'-bis(5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalenedicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 7. The composition of matter as set forth in claim 4 in which said polymer compound is polyphenyl oxide and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is α,α'-bis(5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalenedicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 8. The composition of matter as set forth in claim 4 in which said polymer compound is an epoxy resin and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is 4,4'-bis(5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalenedicarboximidomethyl)-2,2'3,3',5,5',6,6'-octachlorodiphenyl ether.
 9. The composition of matter as set forth in claim 4 in which said polymer compound is acrylonitrilebutadiene-styrene terpolymer and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicidicarboxylic acid is 4,4'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximidomethyl)-2,2',3,3',5,5',6,6'-octachlorodiphenylamine.
 10. A composition of matter comprising a polymer and a haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid having the formula: ##STR14## in which A, X, and Y are independently selected from the group consisting of hydrogen or halogen, at least one A and two X's being halogen; Z is selected from the group consisting of oxygen, sulfur, amino and lower alkyl radicals; m is 1; n is 0; and p is 0 or
 1. 11. The composition of matter as set forth in claim 4 in which said haloaryl imide of polyhalo-substituted polyhydropolycyclicdicarboxylic acid is present in said composition of matter in a range of from about 5% to about 40% by weight of the composition of matter.
 12. The composition of matter as set forth in claim 4 in which said polymer compound is polypropylene and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is selected from the group consisting of α,α'-bis[5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphtalene-dicarboximido]-2,3,5,6-tetrachloro-p-xylene and α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 13. The composition of matter as set forth in claim 4 in which said polymer compound is polypropylene and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is selected from the group consisting of α,α'-bis[5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphtahalene-dicarboximido]-2,3,5,6-tetrachloro-p-xylene, α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,3,5,6-tetrachloro-p-xylene, and α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,4,5,6-tetrachloro-m-xylene.
 14. The composition of matter as set forth in claim 4 in which said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is α,α'-bis(5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalenedicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 15. The composition of matter as set forth in claim 4 in which said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is selected from the group consisting of α,α'-bis[5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalene-dicarboximido]-2,3,5,6-tetrachloro-p-xylene and α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 16. The composition of matter as set forth in claim 4 in which said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is selected from the group consisting of α,α'-bis[5,6,7,8,9,9-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphthalene-dicarboximido]-2,3,5,6-tetrachloro-p-xylene, α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,3,5,6-tetrachloro-p-xylene, and α,α'-bis(1,4,5,6,7,7-hexachlorobicyclo-[2.2.1]-5-heptene-2,3-dicarboximido)-2,4,5,6-tetrachloro-m-xylene.
 17. The composition of matter as set forth in claim 1 in which said polymer compound is a styrene copolymer and said haloaryl imide of a polyhalo-substituted polyhydropolycyclicdicarboxylic acid is α,α'-bis(5,6,7,8,9,9,-hexachloro-1,2,3,4,4a,5,8,8a-octahydro-5,8-methano-2,3-naphtalenedicarboximido)-2,3,5,6-tetrachloro-p-xylene.
 18. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing from about 0.5 to about 10 weight percent of an antimony-containing compound and from about 5 to about 50 weight percent of an imide of a halogen substituted polyhydrocyclicdicarboxylic acid having the formula: ##STR15## in which X is halogen or hydrogen, at least two X's being halogen; Y is halogen or hydrogen; m is 1 to 2; n ranges from 0 to 2; R is selected from the group consisting of hydrogen and monovalent R'; and R' is selected from the group consisting of alkyl and aminoalkyl of from 1 to 20 carbon atoms, polyalkenepolyamino, aryl, haloaryl, alkoxyaryl, polyarylenepolyamino of from 1 to 3 carbocyclic rings, and aminocyclopolyalkyl and polyalkenepolyamino having from 4 to 8 carbon atoms on the ring.
 19. The flame retardant composition of claim 18 in which said halogen is chlorine.
 20. The flame retardant composition of claim 18 in which said halogen is bromine.
 21. The flame retardant composition of claim 18 in which said antimony-containing compound is antimony trioxide.
 22. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing from about 0.5 to about 25 weight percent of an antimony-containing compound and from about 5 to about 37.5 weight percent of an imide of a halogen substituted polyhydrocyclicdicarboxylic acid having the formula: ##STR16## in which X is halogen or hydrogen, at least two X's being halogen; Y is halogen or hydrogen; m is 1; n is 0 and R' is selected from the group consisting of alkyl of from 1 to 20 carbon atoms, polyalkenepolyamino, aryl, haloaryl, alkoxyaryl, polyarylenepolyamino of from 1 to 3 carbocyclic rings and polyalkenepolyamino having from 4 to 8 carbon atoms on the ring.
 23. The flame retardant composition of claim 22 in which said halogen is chlorine.
 24. The flame retardant composition of claim 22 in which said halogen is bromine.
 25. The flame retardant composition of claim 22 in which said antimony-containing compound is antimony trioxide.
 26. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing an antimony-containing compound and an amide selected from the group consisting of ##STR17## wherein X is chlorine and wherein R' is a divalent organic radical.
 27. A flame retardant composition according to claim 26 containing from about 0.5 to about 25% by weight of said antimony compound and from about 5 to about 37.5% by weight of said imide.
 28. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing an antimony-containing compound and an imide selected from the group consisting of ##STR18## wherein X is chlorine and wherein R' is selected from the group consisting of alkyl and aminoalkyl, polyalkenepolyamino, aryl, haloaryl, alkoxyaryl and aminocyclopolyalkyl.
 29. A flame retardant composition according to claim 28 containing from about 0.5 to about 25% by weight of said antimony compound and from about 5 to about 37.5% by weight of said imide.
 30. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing an antimony-containing compound and an imide of the formula ##STR19## wherein X is chlorine and wherein R' is a divalent organic radical.
 31. A flame retardant composition according to claim 30 containing from about 0.5 to about 25% by weight of said antimony compound and from about 5 to about 37.5% by weight of said imide.
 32. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing an antimony-containing compound and an imide of the formula ##STR20## wherein X is chlorine and wherein R' is selected from the group consisting of alkyl and aminoalkyl, polyalkenepolyamino, aryl, haloaryl, alkoxyaryl and aminocyclopolyalkyl.
 33. A flame retardant composition according to claim 32 containing from about 0.5 to about 25% by weight of said antimony compound and from about 5 to about 37.5% by weight of said imide.
 34. A flame retardant composition of matter selected from the group consisting of polyolefins and ABS containing an antimony-containing compound and an imide selected from the group consisting of ##STR21## in which x is chlorine or hydrogen, at least two x's being chlorine, and R' is selected from the group consisting of alkyl and aminoalkyl, polyalkenepolyamino, aryl, haloaryl, alkoxyaryl and aminocyclopolyalkyl.
 35. A composition as claimed in claim 1 wherein each X is chlorine.
 36. A composition as claimed in claim 1 wherein said flammable material is a polymer.
 37. A composition as claimed in claim 36 wherein said polymer is polyethylene.
 38. A composition as claimed in claim 36 wherein said polymer is polypropylene.
 39. A composition as claimed in claim 36 wherein said polymer is an acrylonitrile-butadiene-styrene polymer.
 40. A composition as claimed in claim 36 wherein said polymer is an ethylene-propylene copolymer.
 41. A composition as claimed in claim 36 wherein said polymer is poly(1,12-dodecamethylene pyromellitimide).
 42. A composition as claimed in claim 36 wherein the composition contains up to about 40% by weight of the bis-imide, based on the weight of the polymer.
 43. A composition as claimed in claim 36 wherein the polymer is irradiation crosslinked.
 44. A composition as claimed in claim 36 wherein the composition contains from 10% to 30% by weight of the bis-imide, based on the weight of the polymer.
 45. A composition comprising a flammable material, a halogen-containing bis-imide and a compound of an element of Group V.
 46. A composition as claimed in claim 45 wherein said compound is an antimony compound.
 47. A composition as claimed in claim 46 wherein said antimony compound is antimony oxide.
 48. A composition as claimed in claim 45 wherein the total weight of the halogen-containing bis-imide and the Group V compound is at most 40% of the weight of the composition. 